PMT TCC TYPE

PMT-316 TCC . PMT-625 TCC

This product identifies a new generation of Sliding Bearings for applications in low and high temperature, thanks to a special coating performed with a system similar to the PVD process. This coating confers to the material an excellent resistance to extreme temperatures while maintaining a good coefficient of static friction even with a dynamic heavy load.

Die hierfür verwendeten metallischen Trägerschichten Produkt sind Aisi 316L und Inconel 625. Mit diesem Art des Produkts, sollte die Welle nicht wärmebehandelt eingereicht werden. It is not recommendable to use oil and grease with these bearings.

PMT-316 TCC – SUPPORTING SHELL: AISI 316L

C

0.03%

Mn

1.8%

S

0.25%

Cr

16.70%

P

0.03%

Ni

10.00%

Si

0.50%

Mo

2.00%

PMT-316 TCC – BEARING SECTION

PMT TCC AISI 316L BACKING

PMT-316 TCC – GRAPHIC LOAD/SPEED

PMT TCC GRAPHIC LOAD/SPEED

PMT-625 TCC – SUPPORTING SHELL: INCONEL 625

C

0.10%

Co

1.00%

Mn

0.05%

Ta+Nb

3.15÷4.15%

Cr

20÷23%

Ni

Rest

Ni

8÷10%

PMT-625 TCC – BEARING SECTION

PMT 625 TCC AISI 316 L

PMT-625 TCC – GRAPHIC LOAD/SPEED

PMT 625 TCC GRAPHIC LOAD/SPEED

The values shown in the graph were determined with a test of constant load, and running for 1000 cycles at three different temperatures: -198 °C, +18 °C and +430 °C.

Vergleichstabelle

PMT-316 TCC

PMT-625 TCC

Aisi 316L
+Tungsten carbide

+ Special Coating

Inconel 625
+Tungsten carbide

+ Special Coating

STÜTZSCHALEC 0.03%, Mn 1.80%
S 0.025%, Cr 16.70%
P 0.03%, Ni 10.00%
Si 0.50%, Mo 2.00%
C 0.10%, Co 1.00%
Mn 0.05%, Mo 8 ÷ 10%
Ta + Nb 3.15 ÷ 4.15%
Cr 20 ÷ 23%, Ni Restante
The given values are nominal values from literature.
SLIDING LAYERS

Vaporization of the special coating. Multilayer deposit on the surface. Minimum hardness 180 HB, and minimum thickness 15 μm.

SHAFT

For an op mal performance the sha surface nishing shall be between Ra 0.40 and 1.60 μm, depending on the di erent applica ons. Hardness 100 – 160 HB5.

Mechanical Properties

WORKING TEMPERATUREmin – 198 °C
max + 430 °C
min – 198 °C
max + 430 °C
COEFFICIENT OF FRICTION0.06-0.120.06-0.12
MAX. SPEED0.40 m/s0.40 m/s
MAX. STATIC LOAD200 N/mm2200 N/mm2

MAX. DYNAMIC LOAD
(max. speed 0.05 m/s)

150 N/mm2150 N/mm2

MAX. DYNAMIC LOAD
(max. speed 0.50 m/s)

100 N/mm2100 N/mm2

Chemical Resistance

HYDROCARBONSExcellentExcellent
HYDROCHLORIC ACID
(concentrate to 10%)
ExcellentExcellent

SULFURIC ACID
(concentrate to 10%)

ExcellentExcellent
METHANEExcellentExcellent
OXYGENExcellentExcellent
SODIUM HYDROXIDEExcellentExcellent
LIQUID NITROGENExcellentExcellent
SOLVENTSExcellentExcellent

Hinweis: Die Informationen in dieser Tabelle gelten als zuverlässig, aber die Bedingungen und Methoden der Verwendung, die außerhalb unserer Kontrolle liegen, können die Ergebnisse verändern. Die Informationen und Daten in dieser Tabelle sind das Ergebnis einer langen und detaillierten Forschung, jedoch F.lli Paris S.r.l. kann nicht für falsche oder unvollständige Daten verantwortlich gemacht werden. Wir behalten uns vor, diese Produkte ohne vorherige Ankündigung zu ändern.