TX TCC Type
TX-316 TCC . TX-625 TCC
This code identifies a line of bearings that are specially manufactured to allow the bonding of a filled PTFE coated fiber (lead free, in accordance to the European Parliament “ELV” directive 2000/53/EC) on four types of backing metal layers, like carbon steel, bronze, stainless steel and Inconel 625.
The Sliding Surface is primarily composed of filled PTFE coated fiber, and other elements to guarantee the high wear resistance. The TX products find their best usage in slow-moving applications, with heavy loads, and where dry operation is required. Thanks to the thick self-lubricating layer up to 0.40 mm, this product has a high wear resistance, and can work in dirty or abrasive environment.
For this product it is not recommended the use of oil, while the use of special grease, such as silicon or lithium soap, is only possible during the assembly.
TX-316 TCC – STÜTZSCHALE: AISI 316L
C |
0.03% |
Mn |
1.80% |
S |
0.025% |
Cr |
16.70% |
P |
0.03% |
Ni |
10.00% |
Si |
0.50% |
Mo |
2.00% |
TX-316 TCC – LAGERABSCHNITT
TX-316 TCC – LAST/GESCHWINDIGKEIT GRAFIK
TX-625 TCC – STÜTZSCHALE: INCONEL 625
C |
0.10% |
Co |
1.00% |
Mn |
0.05% |
Ta+Nb |
3.15÷4.15% |
Cr |
20÷23% |
Ni |
Rest |
Mo |
8÷10% |
TX-625 TCC – LAGERABSCHNITT
TX-625 TCC – LAST/GESCHWINDIGKEIT GRAFIK
Vergleichstabelle
TX-316 CCC |
TX-625 CCC |
|
|---|---|---|
|
Aisi 316L |
Inconel 625 |
|
| STÜTZSCHALE | C 0.03%, Mn 1.80% S 0.025%, Cr 16.70% P 0.03%, Ni 10.00% Si 0.50%, Mo 2.00% |
C 0.10%, Co 1.00% Mn 0.05%, Mo8 ÷ 10% Ta + Nb 3.15 ÷ 4.15% Cr 20 ÷ 23%, Ni Rest |
| The given values are nominal values from literature. | ||
| SLIDING LAYERS |
Special fabric with filled PTFE, colour black-gray, thickness 400 μm, heavy load capacity and self-lubricating under dry operation. |
|
| SINTERING | Special adhesive between the ber and the backing steel, thickness 60 μm. | |
| SHAFT | For an optimal performance the shaft surface finishing shall be between Ra 0.40 and 1.60 μm, depending on the different applications. Hardness 80 – 160 HB5. | |
Mechanical Properties
| WORKING TEMPERATURE | min – 180 °C max + 260 °C | min – 180 °C max + 260 °C |
| COEFFICIENT OF FRICTION | 0.03-0.10 | 0.03-0.10 |
| MAX. SPEED | 0.50 m/s | 0.50 m/s |
| MAX. STATIC LOAD | 300 N/mm2 | 400 N/mm2 |
| MAX. DYNAMIC LOAD (max. speed 0.05 m/s) |
190 N/mm2 | 190 N/mm2 |
| MAX. DYNAMIC LOAD (max. speed 0.50 m/s) |
100 N/mm2 | 100 N/mm2 |
Chemical Resistance
| HYDROCARBONS | Excellent | Excellent |
| HYDROCHLORIC ACID (concentrate to 10%) |
Excellent | Excellent |
| SULFURIC ACID (concentrate to 10%) |
Excellent | Excellent |
| METHANE | Excellent | Excellent |
| OXYGEN | Excellent | Excellent |
| SODIUM HYDROXIDE | Excellent | Excellent |
| LIQUID NITROGEN | Excellent | Excellent |
| SOLVENTS | Good | Good |
Hinweis: Die Informationen in dieser Tabelle gelten als zuverlässig, aber die Bedingungen und Methoden der Verwendung, die außerhalb unserer Kontrolle liegen, können die Ergebnisse verändern. Die Informationen und Daten in dieser Tabelle sind das Ergebnis einer langen und detaillierten Forschung, jedoch F.lli Paris S.r.l. kann nicht für falsche oder unvollständige Daten verantwortlich gemacht werden. Wir behalten uns vor, diese Produkte ohne vorherige Ankündigung zu ändern.