PMT TCC TYPE

PMT-316 TCC . PMT-625 TCC

This product identifies a new generation of Sliding Bearings for applications in low and high temperature, thanks to a special coating performed with a system similar to the PVD process. This coating confers to the material an excellent resistance to extreme temperatures while maintaining a good coefficient of static friction even with a dynamic heavy load.

Les supports métalliques de base utilisés pour ces produits sont l’acier inoxydable AISI 316L et l’Inconel 625. Avec ce type de produit, il ne faut pas durcir thermiquement l’arbre It is not recommendable to use oil and grease with these bearings.

PMT-316 TCC – COQUE D’APPUI: AISI 316L

C

0.03%

Mn

1.8%

S

0.25%

Cr

16.70%

P

0.03%

Ni

10.00%

Si

0.50%

Mo

2.00%

PMT-316 TCC – SECTION DES PALIERS LISSES

PMT TCC AISI 316L BACKING

PMT-316 TCC – GRAPHIQUE CHARGE/VITESSE

PMT TCC GRAPHIQUE CHARGE/VITESSE

PMT-625 TCC – COQUE D’APPUI: INCONEL 625

C

0.10%

Co

1.00%

Mn

0.05%

Ta+Nb

3.15÷4.15%

Cr

20÷23%

Ni

Rest

Ni

8÷10%

PMT-625 TCC – SECTION DES PALIERS LISSES

PMT 625 TCC AISI 316 L

PMT-625 TCC – GRAPHIQUE CHARGE/VITESSE

PMT 625 TCC GRAPHIQUE CHARGE/VITESSE

The values shown in the graph were determined with a test of constant load, and running for 1000 cycles at three different temperatures: -198 °C, +18 °C and +430 °C.

Tableau de comparaison

PMT-316 TCC

PMT-625 TCC

Aisi 316L
+Tungsten carbide

+ Special Coating

Inconel 625
+Tungsten carbide

+ Special Coating

COQUE D’APPUI C 0.03%, Mn 1.80%
S 0.025%, Cr 16.70%
P 0.03%, Ni 10.00%
Si 0.50%, Mo 2.00%
C0.10%, Co 1.00%
Mn 0.05%, Mo 8 ÷ 10%
Ta + Nb 3.15 ÷ 4.15%
Cr 20 ÷ 23%, Ni Restante
The given values are nominal values from literature.
SLIDING LAYERS

Vaporization of the special coating. Multilayer deposit on the surface. Minimum hardness 180 HB, and minimum thickness 15 μm.

SHAFT

For an op mal performance the sha surface nishing shall be between Ra 0.40 and 1.60 μm, depending on the di erent applica ons. Hardness 100 – 160 HB5.

Mechanical Properties

WORKING TEMPERATURE min – 198 °C
max + 430 °C
min – 198 °C
max + 430 °C
COEFFICIENT OF FRICTION 0.06-0.12 0.06-0.12
MAX. SPEED 0.40 m/s 0.40 m/s
MAX. STATIC LOAD 200 N/mm2 200 N/mm2

MAX. DYNAMIC LOAD
(max. speed 0.05 m/s)

150 N/mm2 150 N/mm2

MAX. DYNAMIC LOAD
(max. speed 0.50 m/s)

100 N/mm2 100 N/mm2

Chemical Resistance

HYDROCARBONS Excellent Excellent
HYDROCHLORIC ACID
(concentrate to 10%)
Excellent Excellent

SULFURIC ACID
(concentrate to 10%)

Excellent Excellent
METHANE Excellent Excellent
OXYGEN Excellent Excellent
SODIUM HYDROXIDE Excellent Excellent
LIQUID NITROGEN Excellent Excellent
SOLVENTS Excellent Excellent

Remarque: Les informations contenues dans ce tableau doivent être considérées comme fiables, mais les conditions et les méthodes d’utilisation indépendantes de notre volonté, peuvent modifier les résultats. Les informations et données contenues dans ce tableau sont le résultat d’une longue et détaillée recherche, mais F.lli Paris S.r.l. ne peut être considéré responsable pour toute donnée incorrecte ou incomplète. Face au développement constant des produits, nous nous réservons le droit de les modifier sans préavis.